產(chǎn)品詳情
聚酰亞胺TPI 薄壁阻燃TPI EXTEM VH1003
EXTEM VH1003M Resin SABIC Innovative Plastics Asia Pacific PEI，
EXTEM? VH1003M resin
聚醚酰亞胺
SABIC Innovative Plastics Asia Pacific
SABIC EXTEM? VH1003M TPI
透明熱塑性聚酰亞胺（TPI）樹脂，玻璃化轉(zhuǎn)變溫度（TG）為247C。該產(chǎn)品具有薄壁FR功能，并具有UL94V0列表。根據(jù)VDE/DIN472第815部分，該材料符合RoHS標(biāo)準(zhǔn)，且無鹵素。
產(chǎn)品說明：
Transparent, Thermoplastic Polyimide (TPI) resin with a glass transition temperature (Tg) of 247C. Internal mold release. This product has thinwall FR capability and has a UL94 V0 listing. This material is RoHS compliant and also halogen free according VDE/DIN 472 part 815. Resin is a Dual-use item and is subject to export control restrictions under both U.S. 15 CFR 774 and Annex I of Reg. (EC) 428/2009 as ECCN 1C008. Diversion contrary to law is prohibited.
添加劑：脫模
特性：無鹵，阻燃性
用途：薄壁部件
機(jī)構(gòu)評(píng)級(jí)：DIN VDE 0472 第815部分
RoHS 合規(guī)
外觀：清晰/透明
加工方法：注射成型
EXTEM? VH1003M resin 物性表
|
物理性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
比重 |
1.30 |
g/cm3 |
ASTM D792, ISO 1183 |
|
熔流率（熔體流動(dòng)速率）(367°C/6.6 kg) |
16 |
g/10 min |
ASTM D1238 |
|
溶化體積流率（MVR）(360°C/5.0 kg) |
8.50 |
cm3/10min |
ISO 1133 |
|
收縮率 |
|
|
內(nèi)部方法 |
|
流動(dòng) 1 |
0.50 到 0.70 |
% |
內(nèi)部方法 |
|
流動(dòng) : 3.20 mm |
0.50 到 0.70 |
% |
內(nèi)部方法 |
|
橫向流動(dòng) : 3.20 mm |
0.50 到 0.70 |
% |
內(nèi)部方法 |
|
吸水率 |
|
|
ISO 62 |
|
飽和, 23°C |
1.8 |
% |
ISO 62 |
|
平衡, 23°C, 50% RH |
0.65 |
% |
ISO 62 |
|
熱性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
載荷下熱變形溫度 |
|
|
|
|
0.45 MPa, 未退火, 6.40 mm |
237 |
°C |
ASTM D648 |
|
1.8 MPa, 未退火, 3.20 mm |
217 |
°C |
ASTM D648 |
|
1.8 MPa, 未退火, 6.40 mm |
230 |
°C |
ASTM D648 |
|
1.8 MPa, 未退火, 64.0 mm 跨距 16 |
228 |
°C |
ISO 75-2/Af |
|
維卡軟化溫度 |
|
|
|
|
-- |
242 |
°C |
ASTM D1525, ISO 306/B50 1217 |
|
可燃性 |
額定值 |
單位制 |
測(cè)試方法 |
|
灼熱絲易燃指數(shù) (3.20 mm) |
960 |
°C |
IEC 60695-2-12 |
|
熱燈絲點(diǎn)火溫度 (3.00 mm) |
850 |
°C |
IEC 60695-2-13 |
|
極限氧指數(shù) |
45 |
% |
ISO 4589-2 |