產(chǎn)品詳情
共聚物PC DMX9455 NA9B049T PC阻燃V0 耐刮擦
DMX9455 NA9B049T特性備注：共聚物、耐刮擦性、阻燃性能
重要參數(shù)： 熔體流動速率:15 g/10min 密度:1.2 g/cm3 吸水率:0.04 % 成型收縮率:0.5 % 缺口沖擊強(qiáng)度:3 拉伸強(qiáng)度:65 MPa 斷裂伸長率:7 % 彎曲強(qiáng)度:120 MPa 彎曲模量:2600 MPa 硬度:108 維卡軟化點(diǎn):139 ℃ 熱變形溫度:119 ℃ 透光率:88 %
共聚物PC DMX9455 NA9B049T PC阻燃V0 耐刮擦
原料技術(shù)數(shù)據(jù)
|
性能項(xiàng)目 |
試驗(yàn)條件[狀態(tài)] |
測試方法 |
測試數(shù)據(jù) |
數(shù)據(jù)單位 |
|
|
物理性能 |
比重 |
|
ASTM D792 |
1.20 |
g/cm3 |
|
|
ISO 1183,ASTM D792 |
1.17 |
g/cm3 |
||
|
特定體積 |
|
ASTM D792 |
0.850 |
cm3/g |
|
|
熔流率 |
300℃/1.2 kg |
ASTM D1238 |
15 |
g/10 min |
|
|
溶化體積流率（MVR） |
300℃/1.2 kg |
ISO 1133 |
13.5 |
cm3/10min |
|
|
收縮率 |
流動: 3.20 mm |
Internal Method |
0.50 到 0.80 |
% |
|
|
吸水率 |
24 hr, 50% RH |
ASTM D570 |
0.040 |
% |
|
|
24 hr, |
ASTM D570 |
0.080 |
% |
||
|
飽和, 23℃ |
ISO 62 |
0.27 |
% |
||
|
平衡, 23℃ |
ASTM D570 |
0.28 |
% |
||
|
平衡, 50% RH |
ASTM D570 |
0.13 |
% |
||
|
平衡, 23℃, 50% RH |
ISO 62 |
0.13 |
% |
||
|
機(jī)械性能 |
洛氏硬度 |
L 計(jì)秤 |
ASTM D785 |
108 |
|
|
M 計(jì)秤 |
93 |
|
|||
|
球壓硬度 |
H 358/30 |
ISO 2039-1 |
128 |
MPa |
|
|
Erichson Scratch Depth - 6N |
|
Internal Method |
14.0 |
µm |
|
|
Pencil Hardness |
|
ASTM D3363 |
H |
|
|
|
拉伸模量 |
|
ASTM D638 |
2900 |
MPa |
|
|
|
ISO 527-2/1 |
2450 |
MPa |
||
|
抗張強(qiáng)度 |
屈服 |
ASTM D638 |
80.0 |
MPa |
|
|
屈服 |
ISO 527-2/50 |
80.0 |
MPa |
||
|
斷裂 |
ASTM D638 |
65.0 |
MPa |
||
|
斷裂 |
ISO 527-2/50 |
60.0 |
MPa |
||
|
伸長率 |
屈服 |
ASTM D638 |
7.0 |
% |
|
|
屈服 |
ISO 527-2/50 |
7.0 |
% |
||
|
斷裂 |
ASTM D638 |
70 |
% |
||
|
斷裂 |
ISO 527-2/50 |
40 |
% |
||
|
彎曲模量 |
50.0 mm 跨距 |
ASTM D790 |
2600 |
MPa |
|
|
|
ISO 178 |
2450 |
MPa |
||
|
彎曲強(qiáng)度 |
|
ISO 178 |
108 |
MPa |
|
|
屈服, 50.0 mm 跨距 |
ASTM D790 |
120 |
MPa |
||
|
抗泰伯磨耗 |
1000 Cycles, 1000 g, CS-17 轉(zhuǎn)輪 |
ASTM D1044 |
10.0 |
mg |
|
|
1000 Cycles, 1000 g, CS-17 轉(zhuǎn)輪 |
Internal Method |
10.0 |
mg |
||
|
簡支梁缺口沖擊強(qiáng)度 |
-30℃ |
ISO 179/1eA |
3.0 |
kJ/m2 |
|
|
23℃ |
|
3.0 |
kJ/m2 |
||
|
簡支梁缺口沖擊強(qiáng)度 |
-30℃ |
ISO 179/1eU |
47 |
kJ/m2 |
|
|
23℃ |
|
無斷裂 |
|
||
|
懸壁梁缺口沖擊強(qiáng)度 |
-30℃ |
ASTM D256 |
30 |
J/m |
|
|
23℃ |
ASTM D256 |
30 |
J/m |
||
|
-30℃ |
ISO 180/1A |
4.0 |
kJ/m2 |
||
|
23℃ |
ISO 180/1A |
5.0 |
kJ/m2 |
||
|
無缺口懸臂梁沖擊 |
23℃ |
ASTM D4812, ISO 180/1U |
無斷裂 |
|
|
|
-30℃ |
ISO 180/1U |
45 |
kJ/m2 |
||
|
裝有測量儀表的落鏢沖擊 |
23℃, Total Energy |
ASTM D3763 |
30.0 |
J |
|
|
熱性能 |
熱變形溫度 |
0.45 MPa, 未退火, 3.20 mm |
ASTM D648 |
133 |
℃ |
|
0.45 MPa, 未退火, 64.0 mm 跨距 |
ISO 75-2/Bf |
131 |
℃ |
||
|
1.8 MPa, 未退火, 3.20 mm |
ASTM D648 |
119 |
℃ |
||
|
1.8 MPa, 未退火, 64.0 mm 跨距 |
ISO 75-2/Af |
118 |
℃ |
||
|
維卡軟化溫度 |
|
ASTM D1525 |
139 |
℃ |
|
|
|
ISO 306/B50 |
138 |
℃ |
||
|
|
ISO 306/B120 |
140 |
℃ |
||
|
Ball Pressure Test |
125℃ |
IEC 60695-10-2 |
Pass |
|
|
|
140℃ |
|
Pass |
|
||
|
線形膨脹系數(shù) |
流動: -40 到 40℃ |
ASTM E831 |
0.000030 |
cm/cm/℃ |
|
|
流動: 23 到 80℃ |
ISO 11359-2 |
0.000030 |
cm/cm/℃ |
||
|
流動:-40 到 40℃ |
ASTM E831 |
0.000070 |
cm/cm/℃ |
||
|
流動: 23 到 80℃ |
ISO 11359-2 |
0.000070 |
cm/cm/℃ |
||
|
比熱 |
|
ASTM C351 |
1400 |
J/kg/℃ |
|
|
導(dǎo)熱系數(shù) |
|
ASTM C177, ISO 8302 |
0.20 |
W/m/K |
|
|
可燃性 |
UL 阻燃等級 |
1.50 mm, Testing by SABIC |
UL 94 |
V-2 |
|
|
3.00 mm, Testing by SABIC |
V-0 |
||||
|
光學(xué)性能 |
折射率 |
|
ASTM D542, ISO 489 |
1.584 |
|
|
透射率 |
2540 µm |
ASTM D1003 |
88.0 |
% |
|
|
霧度 |
2540 µm |
ASTM D1003 |
< 0.80 |
% |
|
共聚物PC DMX9455 NA9B049T PC阻燃V0 耐刮擦